Acronimo Nombre Acronimo Subfamilia                                          
LLDPE POLIETILENO BAJA DENSIDAD LINEAL PARA INYECCIÓN LLDPE IM -120 87-96 1100-1350 120 1400-2000                 NO BREAK   D 52-55   - -   >700
POM POLIÓXIDO DE METILENO (HOMOPOLÍMERO) POM HO   181   25-75 9500-12000 18000 @10% 14000 520 670 380-430       1.3-2.3 M 94    100 255 338 5.5 500 (90 mil)
POM POLIÓXIDO DE METILENO (COPOLÍMERO) POM CO   175   40-75 8800 16000 @10% 13000 410 450 375       1.0-1.5 M 78   85 230 316 5.5 500 (90 mil)
POM POLIÓXIDO DE METILENO (HOMOPOLÍMERO), CON 20% FV POM HO FV   181 8500 7   18000 @10% 15000 1000   730       0.8 M 90   36-81 315 354   490
POM POLIÓXIDO DE METILENO (COPOLÍMERO), CON 20% FV POM CO FV   175 18500 3   17000 @10% 28000 1250   1100       1.8 M 79     325 331   580
ABS ACRILONITRILO ESTIRENO BUTADIENO ABS   110-125 5000-8000 25-may 4000-6000 6500-7500 9000-14000 320-400 130-310 300-400       3.0-12 R 100-120   65-95 195-225 ANNEALED 210-245 ANNEALED   350-500
ABS ACRILONITRILO ESTIRENO BUTADIENO ALTA TEMPERATURA ABS HH   110-125 6000-7500 20-mar 5500-7000 7200-10000 10000-13000 300-350 190-440 300-400       2.0-6.5 R 100-115   60-93 220-240 ANNEALED 230-245 ANNEALED 4.5-8.0 350-500
ABS ACRILONITRILO ESTIRENO BUTADIENO MEDIO IMPACTO ABS MI   105-115 6000-7500 25-may 5000-6000 1800-12500 11000-13000 300-400 200-450 350-400       3.0-6.0 R 107-115   80-100 200-220 ANNEALED 215-225 ANNEALED   350-500
ABS ACRILONITRILO ESTIRENO BUTADIENO ALTO IMPACTO ABS HI   100-110 4800-6300 may-70 4000-5000 4500-800 8000-11000 230-330 140-300 250-350       6.5-7.5 R 85-105   95-110 205-215 ANNEALED 210-225 ANNEALED   350-500
ABS ALEACIÓN ABS/PVC ABS/PVC     5800       9600 330   340       10.5 R 100    46       500
ABS ACRILONITRILO ESTIRENO BUTADIENO CON RETARDANTE A LA FLAMA ABS FR   110-125 5000-8000 2.25 4000-6000 6500-7500 9000-14000 320-400 130-310 300-400       3.0-12 R 100-120   65-95 195-225 ANNEALED 210-245 ANNEALED   350-500
ABS ACRILONITRILO ESTIRENO BUTADIENO CROMABLE ABS PL   100-110 6000-6400       10500-11500 330-380   340-390       5.0-5.3 R 103-109   47-53 204-215 ANNEALED 215-222 ANNEALED   420-550
ASA ACRILONITRILO ESTIRENO ACRILATO ASA   100 6000-8000 20-60 5000-6000 9500-21500 10000-120000             6.0-8.0 R 102-108   10-jun 204-220 ANNEALED 215-225 ANNEALED   350-500
PMMA POLIMETIL METACRILATO PMMA IM   90-150 7000-11000 10-feb   12000-18000 13000-19000 380-450 370-460 420-460       0.3-0.5 M 85-105   50-90 165-210 175-225 4.0-6.0 400-500
PMMA POLIMETIL METACRILATO COPOLÍMERO ALTA RESISTENCIA ALTO IMPACTO  PMMA CO HI   80-100 5000-9000 20-70   4000-14000 7000-13000 200-400 350-460 200-380       0.8-2.5 R 105-120   50-80 165-203 180-205 4.0-5.0 380-500
PMMA POLIMETIL METACRILATO CON ALTA RESISTENCIA TÉRMICA PMMA HH   100-125 10000 05-mar   17000 12000-16000 240-370   460-500       0.3-0.4 m 95-105   50-60 190-220 205-240 4.5 400-500
CET ESTIRENO ACRILATO COPOLÍMERO CET   100-105 10000 3   11000-15000 16000-19000 430 240-370 260-380       0.3 M 75   60-80 205-212   4.0-5.0 450
SAN ESTIRENO ACRILONITRILO (COPOLÍMERO) SAN   115-125 9000-12000 04-ene   14000-17000 14000-17000 400-560 530 550       0.35-0.50 M 80-90   36-38 190-220   2.9 400-500
PS POLIESTIRENO GPPS   85-105 5300-7900 02-ene   11500-16000 8000-14000 350-485   380-450       0.25-0.4 M 60-75   70-80 165-212   03-feb 600
PS POLIESTIRENO MEDIO IMPACTO MIPS   90-110 3200-4900 13-50 2900-4900 4000-9000 5300-9400 260-465   280-450       0.6-3.6 M 10-68   70-101 165-200 170-200 05-mar 450
PS POLIESTIRENOALTO IMPACTO HIPS                                          
PS POLIESTIRENO ALTA TEMPERATURA PSHH   110-125 5000-7800 feb-60   11500-16000 8900-14000 320-460   340-470       0.4-3.4 L 80-108   60-70 200-248     500
SBC ESTIRENO BUTADIENO COPOLÍMERO SBC F     3400-4000 15-100       180-200           0.4       160     300
PE POLIETILENO BAJA DENSIDAD LDPE   95-130 600-2300 90-800 800-1200     14-38   ago-60       NO BREAK   D 40-51 100-220 90-105 100-121 8 450-1000
EVA ETILENO VINIL ACETATO (COPOLÍMERO) EVA 65-90   1400-2800 550-900       20-120   20-ene       NO BREAK   D 17-45 160-200 93 140-147   620-760
EEA COPOLÍMERO ETILENO ACRILATO DE ETILENO EEA   75 1600-2100 700-750   3000-3600   4-7.5           NO BREAK   D 27-36 160-250       450-550
POP RESINA IONOMÉRICA POP 90-96   3500-4500 350-450       20-60   30-50       15-jun   D 50-65 120 100-120   5.8  
PE POLIETILENO ALTA DENSIDAD HDPE   120-140 3100-5500 20-130 3000-4000 2700-3600   60-180   100-260       0.5-20   D 60-70 110-130 110-130 140-190 12-nov 450-500
PE POLIETILENO MEDIA DENSIDAD MDPE   120-140 1200-3500 50-600 1000-2200     22-55   60-115       0.5-16   D 50-60 140-160 105-120 120-165 10-ago 450-1000
PE POLIETILENO ULTRA ALTO PESO MOLECULAR UHMWPE   125-135 5600 450-525 3100-4000         130-140       NO BREAK R 50    130 110-120 155-180   710
PP POLIPROPILENO HOMOPOLÍMERO PP HO IM 168   4500-6000 100-600 4500-5400 5500-8000 6000-8000 165-225 150-300 170-250 50 35   0.4-1.0 R 80-102   81-100 120-140 225-250 2.8 600
PP POLIPROPILENO COPOLÍMERO IMPACTO INYECCIÓN PP IMCO IM 120-135   2800-4400 350-500 2800-4400 4000-6500       90-150       1.0-15 R 50-85   83-100 124-133 165-192 04-feb 600
PP POLIPROPILENO COPOLÍMERO RANDOM INYECCIÓN PP RACO IM 160-168   4000-5500 200-700 3500-4300 5500-8000 5000-7000 100-170   130-200 40 30   1.0-20.0 R 50-96   68-95 115-140 185-220 3.5-4.0 600
BT POLIBUTENO 1                                            
PIB POLI-ISO BUTILENO                                            
PMP POLI ISOBUTILENO-ETILENO                                            
PTFE POLITETRAFLUOROETILENO   220   4500-6000 80-250   4600-7400 7400-9300 150-300           2.5-2.7 R 75-95       258 4.7-5.3 500-600
FEP COPOLÍMERO TETRAFLUJO RETILENO-ESAFLUOROPR.   275   2700-3100 250-330   2200   50   80-95       NO BREAK   D 60-65     158 6 500-600
PCTFE POLICLOROTRIFLUORETILENO   220   4500-6000 80-250   4600-7400 7400-9300 150-300           2.5-2.7 R 75-95       258 4.7-5.3 500-600
PVF POLIFLUORURO DE VINIL                                            
PVDF POLIFLUORURO DE VINILIDENO   156   5500-7400 25-500   8700-10000 8600-11000 120 120 200       3.6-4.0   D 80 85 176-194 234-284 4.5-5.8 260
CA ACETATO DE CELULOSA   230   1900-9000 jun-70   3000-8000 2000-16000     1200-4000       1.0-7.8 R 34-125   80-180 111-195 120-209 08-abr 250-600
CP PROPINATO DE CELULOSA   190   2000-7800 29-100   2400-7000 2900-11400 60-215   120-350       0.5-NB R 10-122   110-170 111-228 147-250 08-abr 300-450
CAB ACETATO BUTIRATO DE CELULOSA   140   2600-6900 40-88   2100-7500 1800-9300 50-200   90-300       1.0-10.9 R 31-116   110-170 113-202 130-227 08-abr 250-400
EC ETICELULOSA   135   2000-8000 may-40     4000-12000             0.4 R 50-115   100-200 115-190 - 3.8-7.0 350-500
PA 66 POLIAMIDA (NYLON 66) PA 66 265   12000 (SECO,0.2% HUM), 11000 (50% HUM) 60 (SECO, 0.2% HUM),    300 (50% HUM) 8000 (SECO, 0.2% HUM), 6500 (50% HUM) 15000 (SECO, 0.2% HUM) YLD. 17000 (SECO, 0.2% HUM), 6100 (50% HUM)     420 (SECO, 0.2% HUM),                     185 (50% HUM)       0.8-1.0 (SECO, 0.2% HUM),                  2.1 (50% HUM) R 120 (SECO, 0.2% HUM), M 83 (50% HUM)   80 167 474 5.8 600
PA 66 POLIAMIDA 66 DE ALTO IMPACTO PA 66 HI 240-260   7000-8000 (SECO,0.2% HUM) 4-80 (SECO, 0.2% HUM), 200-300 (50% HUM)                                  
PA 66 POLIAMIDA 66 CON REFUERZO DE FIBRA DE VIDRIO PA 66 C FV 265   12000 (SECO,0.2% HUM), 11000 (50% HUM) 60 (SECO, 0.2% HUM),    300 (50% HUM) 8000 (SECO, 0.2% HUM), 6500 (50% HUM) 15000 (SECO, 0.2% HUM) YLD. 17000 (SECO, 0.2% HUM), 6100 (50% HUM)                            
PA 66/6 COPOLIAMIDA 66/6 PA 66/6 240   7400-14400 (SECO,0.2% HUM) 40 (SECO, 0.2% HUM),    300 (50% HUM)       3150-410(SECO, 0.2% HUM)   150-410 (SECO, 0.2% HUM)       0.7 (SECO, 0.2% HUM), NO SE ROMPE (50% HUM) R 119 (SECO, 0.2% HUM), R 83 (50% HUM)     170 (SECO, 0.2% HUM) 430 (SECO, 0.2% HUM)   400 (SECO, 0.2% HUM)
PA 6 POLIAMIDA (NYLON 6) PA 6 216   11800 (SECO, 0.2% HUM), 10000 (50% HUMEDAD) 30-100 (SECO. 0.2% HUM), 10000 (50% HUM) 8000 (SECO, 0.2% HUM), 5000 (50% HUM) 13000-16000              (SECO, 0.2% HUM) 14000 (SECO, 0.2 % HUM), 5000 (50% HUM) 380 (SECO, 0.2% HUM),                     100 (50% HUM) 250 (50% HUM) 390 (SECO, 0.2% HUM),                     140 (50% HUM)       0.6-1.0 (SECO, 0.2% HUM),                  3.0 (50% HUM) R 119 (SECO, 0.2% HUM)   80-83 155-185 (SECO, 0.2% HUM) 365-375 (SECO, 0.2% HUM) 5.8 400 (SECO, 0.2% HUM)
PA 6 POLIAMIDA 6 CON REFUERZO DE FIBRA DE VIDRIO PA 6 C FV 216   25000 (SECO, 0.2% HUM), 13000 (50% HUMEDAD) 3-6 (SECO. 0.2% HUM)   19000   (SECO, 0.2% HUM) 33000 (SECO, 0.2 % HUM), 18000 (50% HUM) 1450 (SECO, 0.2% HUM), 800 (50% HUM)   1500 (SECO, 0.2% HUM),  800 (50% HUM)       1.8-NO SE ROMPE (SECO, 0.2% HUM) M 101 (SECO, 0.2% HUM), M 78 (50% HUM)   20-30 410 (SECO, 0.2% HUM) 430(SECO, 0.2% HUM) 5.8 400 (SECO, 0.2% HUM)
PA 6 POLIAMIDA 6 ALTO IMPACTO PA 6 HI 216   7500-11000 (SECO, 0.2% HUM) 150-270 (SECO. 0.2% HUM)     5000-12000 (SECO, 0.2 % HUM)     110-320 (SECO, 0.2% HUM) 60-130 (SECO, 0.2% HUM)     3.0 (SECO, 0.2% HUM) R 81-110 (SECO, 0.2% HUM)   30-40 113-130 (SECO, 0.2% HUM) 260-350 (SECO, 0.2% HUM)   450 (SECO, 0.2% HUM)
PA 11 POLIAMIDA (NYLON 11) PA 11 194   8000 (SECO, 0.2% HUM) 300 (SECO, 0.2% HUM)       185 (SECO, 0.2% HUM) 180 (SECO, 0.2% HUM) 150 (SECO, 0.2% HUM)       1.8 (SECO, 0.2% HUM) R 108 (SECO, 0.2% HUM)   100 130 (SECO, 0.2% HUM) 300 (SECO, 0.2% HUM) 8 425 (SECO, 0.2% HUM)
PA 6/10 POLIAMIDA (NYLON 610) PA 6/10                                          
PA 6/12 POLIAMIDA (NYLON 612) PA 6/12 217   8800 (SECO, 0.2% HUM) 150 (SECO, 0.2% HUM),  300 (50% HUM)       290 (SECO, 0.2% HUM),                     180 (50% HUM)   290 (SECO, 0.2% HUM),                     100 (50% HUM)       1.0 (SECO, 0.2% HUM),                        1.4 (50% HUM) R 114 (SECO, 0.2% HUM)     180 (SECO, 0.2% HUM) 330 (SECO, 0.2% HUM) 5.2 400 (SECO, 0.2% HUM)
PA 12 POLIAMIDA (NYLON 12) PA 12 179   8000-9000 (SECO, 0.2% HUM) 300 (SECO, 0.2% HUM)       180 (SECO, 0.2% HUM)   165 (SECO, 0.2% HUM)       2.0-5.5 (SECO, 0.2% HUM) R 106-109             (SECO, 0.2% HUM)   100 130 (SECO, 0.2% HUM) 293 (SECO, 0.2% HUM) 5.2 450 (SECO, 0.2% HUM)
PU POLIURETANO PU                                          
PU POLIURETANO LÍQUIDO LIQUID THERMOSET   175-10000 100-1000   20000 700-4500 10-100 10-100 10-100       25 TO FLEXIBLE   10A-90D 100-200 VARIES OVER WIDE RANGE.   5 300-500
PU POLIURETANO INSATURADO UNSATURATED THERMOSET   10000-11000 06-mar     19000     10-jun       0.4   30-35 BARCOL   190-200      
PET POLIETILEN TEREFTALATO UNFILLED 245 73 8500-10500 50-300   11000-15000 14000-18000 400-600   350-450       0.25-0.65 M 94-101   65 100-106 (ANNEALED)   3.6 -
PET POLIETILEN TEREFTALATO PET FV 245   23000 3   25000 33500 1440   1300 520 390   1.9 M 100   29 435     550
PBT POLIBUTILENTEREFTALATO UNFILLED 232-267   8200 50-300   8600-14500 12000-16700 280   330-400       0.8-1.0 M 68-78   60-95 122-185 240-375 4.2-6.9 420-550
PBT POLIBUTILENTEREFTALATO PBT FV 232-267   17000-19000 04-feb   18000-23500 26000-29000 1300   1100-1200       1.3-1.6 M 90   25 428 437 7 460-550
PC POLICARBONATO ALTA VISCOSIDAD PC HV   150 9500 110 9000 12500 13500 345 350 340       16 @ 1/8 in. M 70   68 270 280 4.7 380
PC POLICARBONATO BAJA VISCOSIDAD PC LV   140 9500 110 9000 12500 13500 345 350 340       14 @ 1/4 in. M 70   68 270 280 4.7 380
PC/ABS   PC/ABS                                          
PVC CLORURO DE POLIVINIL PVC                                          
PVC CLORURO DE POLIVINIL (RÍGIDO) PVC R   75-105 6000-7500 40-80   8000-13000 10000-16000 350-600   300-500       0.4-20   D 65-85 50-100 140-170   3.5-5.0 350-500
PVC CLORURO DE POLIVINIL          (FLEXIBLE, UNFILLED) PVC F   75-105 1500-3500 200-450   900-1700               VARIES OVER WIDE RANGE   A 50-100 70-250     04-mar 300-400
PVC CLORURO DE POLIVINIL            (FLEXIBLE, FILLED) PVC F   75-105 1000-3500 200-400   1000-1800               VARIES OVER WIDE RANGE   A 50-100       04-mar 250-300
PVCA CLORURO DE POLIVINIL (COPOLÍMERO)                                            
PVC-PP CLORURO VINILO POLIPROPILENO (COPOLÍMERO)                                            
PV DC CLORURO DE POLIVINILIDENO                                            
PE OC POLIETERE CLORURATO                                            
PV CC CLORURO DE POLIVINIL CLORURATO     110 7500-9000 abr-65   9000-22000 14500-17000 360-475 335-600 380-450       1.0-5.6 R 117-122   68-76 202-234 215-247 3.3  
PPO POLIÓXIDO DE FENILENO PPO                                          
PPO POLIÓXIDO DE FENILENO    (TRANSICIÓN VÍTREA BAJA) PPO LGT   110 7800 50   12000-16400 12800 380   360-400 260     5 R 115   38-68 212 230 3.8 400
PPO POLIÓXIDO DE FENILENO    (TRANSICIÓN VÍTREA ALTA) PPO HGT   135 9600 60   16400 13500 355   360-400 305     5 R 119   33-59 265 279 5.2 500-550
PPO POLIÓXIDO DE FENILENO         (IMPACTO MODIFICADO) PPO IM   135 7000-8000 35   10000 8200-11000 345-360   325-345       07-jun L 108, M 93     190-275 205-245   530
PPO POLIÓXIDO DE FENILENO (30% FV) PPO FV   100-110 17000-18500 05-mar   17900 20000-23000 1200   1100-1500 1000     1.7-2.3 R 115-116   14-25 275-317 285 3.8-4.1 630
PPS SULFURO DE POLIFENILENO PPS   220   60 10400   12400 310   330       12     31 400     370
PPSU POLISULFONO PPSI   200   50-100 10200 13900 15400 360 370 390       1.2 M 69, R 120   52-56 345 358 2.8 425
PE  POLIETILENO BAJA DENSIDAD EXTRUSIÓN PARA PELÍCULA LDPE EG                                          
DULCE PRUEBA                                            
LLDPE POLIETILENO BAJA LINEAL DENSIDAD EXTRUSION PELICULA LLDPE F   95-102 3480 600-800 1450