Acronimo |
Nombre |
Acronimo Subfamilia |
Densidad |
Punto Fusion |
Precal en Horas |
Precal en C° |
Temp.Zon1 |
Temp.Zon2 |
Temp.Zon3 |
Temp.Zon4 |
Temp.MoldeC |
Temp.MoldeC2 |
Temp.MoldeC3 |
Pres.Inyeccion |
Presion 2a |
Contra Presion |
Vel.Inyeccion |
Punto de Inyeccion |
Contra % |
Recup.Desecho |
Efecto a luz |
Proce Transf. |
Pega Ensamblado |
Metalizado |
Flamabilidad |
Relacion L/D |
Relacion C |
Vel.Husillo |
Relacion Soplado |
Abertura Dado |
Obs.Proceso |
PE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR EXTRUSIÓN PELÍCULA |
HMWPE F |
0.951 |
130-135 (FUS) |
|
|
50 |
200 |
210 |
225 |
|
|
|
|
|
|
|
|
|
|
|
03-feb |
|
|
|
|
|
|
|
|
|
PE |
COMPUESTO DE
POLIETILENO ALTA DENSIDAD PARA TUBERÍA |
HDPE EG T |
0.941-0.96 |
130-135 (FUS) |
|
|
50 |
160 |
180 |
190 |
200 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
2 |
|
|
LENTA |
|
|
|
|
|
|
PE |
POLIETILENO ALTA
DENSIDAD EXTRUSION |
HDPE EG |
0.941-0.96 |
130-135 (FUS) |
|
|
50 |
160 |
180 |
190 |
200 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
2 |
|
|
LENTA |
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD EXTRUSIÓN PARA LÁMINA |
HDPE ESG |
0.941-0.96 |
130-135 (FUS) |
|
|
50 |
200 |
210 |
222 |
30 |
|
|
|
|
|
|
|
|
|
|
7 |
|
|
LENTA |
|
|
|
|
|
|
PE |
POLIETILENO ALTA
DENSIDAD HOMOPOLÍMERO EXTRUSIÓN/SOPLO CUERPO HUECO |
HDPE HO BM |
0.955-0.960 |
130 |
|
|
160 |
170 |
180 |
190 |
70 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
|
|
|
LENTA |
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD COPOLÍMERO EXTRUSIÓN/SOPLO CUERPO HUECO |
HDPE CO BM |
0.941-0.96 |
130 |
|
|
160 |
170 |
180 |
190 |
70 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
|
|
|
LENTA |
|
|
|
|
|
|
POM |
POLIÓXIDO DE
METILENO (HOMOPOLÍMERO) |
POM HO |
1.425 |
175 (FUS) |
06-feb |
70-120 |
160-180 |
180-200 |
190-210 |
200-230 |
80/120 |
|
|
700-1400 |
SEGÚN ESPESOR
PIEZA |
100/200 kg/cm² |
CAPILAR ALTA |
CAPIL. PARA PIEZA
PEQ. |
2 |
10-15 % TRITURADO |
BLANQUEA |
1-2-3-8-10-12 |
EC870 DUPONT 4695 |
BAJO VACÍO |
ALTA CON VAPORES TÓXICOS |
|
|
|
|
|
|
POM |
POLIÓXIDO DE
METILENO (COPOLÍMERO) |
POM CO |
1.41 |
163 (FUS) |
06-feb |
70-120 |
160-180 |
180-200 |
190-210 |
200-230 |
90/120 |
|
|
700-1400 |
|
|
|
|
2.5 |
10-15 % TRITURADO |
BLANQUEA |
1-2-3-8-10-13 |
EC870 DUPONT 4696 |
BAJO VACÍO |
ALTA CON VAPORES TÓXICOS |
|
|
|
|
|
|
POM |
POLIÓXIDO DE
METILENO (HOMOPOLÍMERO), CON 20% FV |
POM HO FV |
1.56 |
175 |
06-feb |
70-120 |
170-190 |
190-210 |
210-230 |
220-245 |
90/120 |
|
|
700-1400 |
|
|
|
|
0.4-1.2 |
8-10 % TRITURADO |
BLANQUEA |
1-2-3-8-10-13 |
EC870 DUPONT 4696 |
|
ALTA CON VAPORES TÓXICOS |
|
|
|
|
|
|
POM |
POLIÓXIDO DE
METILENO (COPOLÍMERO), CON 20% FV |
POM CO FV |
1.61 |
181 |
06-feb |
70-120 |
170-190 |
190-210 |
210-230 |
220-245 |
90/120 |
|
|
700-1400 |
|
|
|
|
0.4-1.8 |
8-10 % TRITURADO |
BLANQUEA |
1-2-3-8-10-13 |
EC870 DUPONT 4696 |
|
ALTA CON VAPORES TÓXICOS |
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO |
ABS |
1.01 |
88-120 |
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50/90 |
|
|
550-1700 |
30-60 % |
100/250 kg/cm² |
1ª LENTA 2ª ALTA |
CAPILAR CÁMARA
CAL. |
0.4-0.8 |
20-30 TRITURADO |
AMARILLEA |
1-2-8-12 |
|
BAJO VACÍO ELECTROLÍT. |
LENTA |
|
2:1 - 2.5:1 |
60 rpm |
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO ALTA TEMPERATURA |
ABS HH |
1.05-1.08 |
110-125 |
04-feb |
70-80 |
230-250 |
250-260 |
260-280 |
270-290 |
50/90 |
|
|
550-1700 |
|
|
|
|
0.4-0.7 |
20-30 TRITURADO |
AMARILLEA |
1-2-8-12 |
|
|
|
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO MEDIO IMPACTO |
ABS MI |
1.00-1.06 |
105-115 |
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50/90 |
|
|
550-1700 |
|
|
|
|
0.4-0.9 |
20-30 TRITURADO |
AMARILLEA |
1-2-8-12 |
|
|
|
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO ALTO IMPACTO |
ABS HI |
1.01-1.04 |
100-110 |
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50/90 |
|
|
550-1700 |
|
|
|
|
0.4-0.9 |
20-30 TRITURADO |
AMARILLEA |
1-2-8-12 |
|
|
|
|
|
|
|
|
|
ABS |
ALEACIÓN ABS/PVC |
ABS/PVC |
|
|
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50-90 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AUTOEXINGIBLE |
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO CON RETARDANTE A LA FLAMA |
ABS FR |
1.16-1.21 |
110-125 |
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50/90 |
|
|
550-1700 |
|
|
|
|
0.4-0.8 |
20-30 TRITURADO |
AMARILLEA |
1-2-8-12 |
|
|
LENTA |
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO CROMABLE |
ABS PL |
1.06-1.07 |
100-110 |
04-feb |
70-80 |
180-200 |
200-220 |
220-260 |
240-275 |
50/90 |
|
|
550-1700 |
|
|
|
|
0.5-0.8 |
|
AMARILLEA |
1-2-8-12 |
|
METALIZADO |
|
|
|
|
|
|
|
ASA |
ACRILONITRILO
ESTIRENO ACRILATO |
ASA |
1.07 |
100 |
04-feb |
80-85 |
220-230 |
230-240 |
240-250 |
260-270 |
60-85 |
|
|
550-1701 |
|
|
|
|
0.4-0.8 |
|
AMARILLEA |
1-2-8-12 |
|
|
LENTA |
|
|
|
|
|
|
PMMA |
POLIMETIL
METACRILATO |
PMMA IM |
1.17-1.20 |
REBLANDECE 90-115 |
08-feb |
70-95 |
160-170 |
180-190 |
200-220 |
240-250 |
30/70 |
|
|
1000-1800 |
LARGA 2-3 MIN |
150/400 kg/cm² |
ALTA |
CANALES GRANDES |
0.2-0.8 |
20% TRITURADO |
ÓPTIMO |
1-2-8-9-12 |
PEGADO SOLDADO |
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
PMMA CO |
POLIMETIL
METACRILATO COPOLÍMERO ALTA RESISTENCIA ALTO IMPACTO |
PMMA CO HI |
1.11-1.18 |
93 Vicat |
08-feb |
70-95 |
200-220 |
210-230 |
230-250 |
260-270 |
30/71 |
|
|
1000-1801 |
LARGA 2-3 MIN |
150/400 kg/cm131 |
ALTA |
|
0.4-.08 |
20% TRITURADO |
DISCRETO |
1-2-8-9-12 |
PEGADO SOLDADO |
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO CON ALTA RESISTENCIA TÉRMICA |
PMMA HH |
1.3-1.4 |
110-121 Vicat |
08-feb |
70-95 |
200-220 |
210-230 |
230-250 |
260-270 |
30/72 |
|
|
100-2050 |
LARGA 2-3 MIN |
150/400 kg/cm132 |
ALTA |
|
0.4-0.7 |
20% TRITURADO |
DISCRETO |
1-2-8-9-12 |
PEGADO SOLDADO |
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
CET |
ESTIRENO ACRILATO
COPOLÍMERO |
CET |
1.09 |
REBLANDECE 100 |
2 |
80 |
270 |
260 |
220 |
180 |
60/90 |
|
|
1000-1800 |
|
150/400 kg/cm² |
ALTA |
CANALES GRANDES |
0.2-0.6 |
20% TRITURADO |
DISCRETO |
1-2-8-9-12 |
PEGADO SOLDADO |
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
SAN |
ESTIRENO
ACRILONITRILO (COPOLÍMERO) |
SAN |
1.08 |
REBLANDECE 90-115 |
04-ene |
70-90 |
160-170 |
190-210 |
240-260 |
270-280 |
50/80 |
|
|
1200-1800 |
30-60 % |
100/200 kg/cm² |
ALTA |
CAPILAR CANAL
CAL. |
0.4-0.7 |
100% |
AMARILLEA |
02/01/2012 |
PEGADO CON TOLUENO |
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
PS |
POLIESTIRENO |
GPPS |
1.04-1.09 |
REBLANDECE 80-90 |
03-ene |
60-80 |
160-170 |
190-200 |
220-240 |
255-280 |
20/50 |
|
|
800-1800 |
30-60 % |
100/200 kg/cm² |
ALTA |
CAPILAR CANAL
CAL. |
0.45-0.55 |
100% TRITURADO |
AMARILLEA |
1-2-3-8-10-12 |
PEGADO CON TOLUENO |
|
LENTA |
|
|
|
|
|
|
MIPS |
POLIESTIRENO
MEDIO IMPACTO |
MIPS EXT |
1.03-1.06 |
90-110 |
03-ene |
60-80 |
160-170 |
190-200 |
220-240 |
255-280 |
216-238 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PS |
POLIESTIRENOALTO
IMPACTO |
HIPS |
1.03-1.07 |
90-111 |
03-ene |
60-80 |
160-170 |
190-200 |
220-240 |
255-280 |
oct-60 |
|
|
800-1800 |
30-60% |
100/200 kg/cm² |
ALTA |
|
0.4-0.7 |
|
|
|
|
|
|
|
|
|
|
|
|
PS |
POLIESTIRENO ALTA
TEMPERATURA |
PSHH |
1.05-1.09 |
110-125 |
03-ene |
60-80 |
160-170 |
190-200 |
220-240 |
255-280 |
20/50 |
|
|
800-1800 |
30-60% |
100/200 kg/cm² |
ALTA |
|
0.4-0.7 |
|
|
|
|
|
|
|
|
|
|
|
|
SBC |
ESTIRENO
BUTADIENO COPOLÍMERO |
SBC F |
0.93-1.10 |
|
1 |
50 |
150-190 |
180-210 |
210-250 |
220-280 |
oct-80 |
|
|
1100-2000 |
50% |
100/200 kg/cm² |
110-2000 |
COLADA CAPILAR |
0.1-0.7 |
80% TRITURADO |
AMARILLEA |
1 |
PEGADO |
|
ARDE |
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD |
LDPE |
0.92-0.93 |
105-115 |
|
|
120-170 |
120-210 |
120-210 |
130-220 |
30/80 |
|
|
600-1800 |
30-60 % |
150/230 kg/cm² |
NORMAL |
COLADA CAPILAR |
1.5-2 |
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
11:1 A 20:1 |
02:01 |
|
|
|
|
EVA |
ETILENO VINIL
ACETATO (COPOLÍMERO) |
EVA |
0.92-0.95 |
|
3 |
70-80 |
140-160 |
155-170 |
170-200 |
210-230 |
25/40 |
|
|
MUY BAJA |
|
MEDIA |
LENTA |
CANAL CORRIENTE |
1.5 |
10% TRITURADO |
DISCRETO |
03/01/2004 |
|
|
LENTA |
|
|
|
|
|
|
EEA |
COPOLÍMERO
ETILENO ACRILATO DE ETILENO |
EEA |
0.93 |
|
|
|
240 |
220 |
190 |
160 |
25/40 |
|
|
1000 |
|
|
|
CANAL CORIENTE |
1.5-3 |
10 % TRITURADO |
DISCRETO |
1-2-3-4 |
|
|
LENTA |
|
|
|
|
|
|
POP |
RESINA IONOMÉRICA |
POP LAMINACION |
0.94-0.96 |
REBLANDECE 75-76 |
|
|
160 |
210 |
220 |
235 |
15-oct |
|
|
|
|
|
|
|
|
|
DISCRETO |
1-2-3-4-8 |
|
|
LENTA |
|
|
|
|
|
|
PE |
POLIETILENO ALTA
DENSIDAD INYECCIÓN |
HDPE |
0.941-0.96 |
130-135 (FUS) |
|
|
180-200 |
190-220 |
200-240 |
230-260 |
oct-70 |
|
|
800-1400 |
30-60 % |
150/250 kg/cm² |
ALTA |
COLADA CAPILAR
C.C. |
1.5-3.5 |
100% TRITURADO |
DISCRETO |
1-2-3-4-5-8-10-12 |
|
BAJO VACÍO |
LENTA |
|
|
|
|
|
|
PE |
POLIETILENO MEDIA
DENSIDAD |
MDPE |
0.931-0.940 |
120-130 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
UHMWPE |
POLIETILENO ULTRA
ALTO PESO MOLECULAR |
UHMWPE |
0.942-0.954 |
125-130 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1.5-3 |
|
|
Compresión |
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO |
PP HO IM |
0.90-0.91 |
185, 152 Vicat |
|
|
200 |
240 |
250 |
260 |
20/90 |
|
|
1200-1800 |
50-70% LARGA |
120/200 kg/cm² |
ALTA/MUY
ALTA(NUCLEADO) |
COLADA CAPILAR |
1.2-2.2 |
10% TRITURADO |
DISCRETO |
1-2-3-4-5-8-10-12 |
SOLDADO |
BAJO VACÍO ELECTROLÍT. |
LENTA |
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO INYECCIÓN |
PP IMCO IM |
0.89-0.91 |
185 |
|
|
200 |
240 |
260 |
280 |
20/90 |
|
|
1500 |
|
|
ALTA/MUY
ALTA(NUCLEADO) |
COLADA CAPILAR |
1.0-2.5 |
10% TRITURADO |
DISCRETO |
1-2-3-4-5-8-10-12 |
SOLDADO |
|
LENTA |
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM INYECCIÓN |
PP RACO IM |
0.89-0.90 |
180 |
|
|
200 |
240 |
260 |
280 |
20/90 |
|
|
1200-1800 |
|
|
ALTA/MUY
ALTA(NUCLEADO) |
COLADA CAPILAR |
1.0-2.5 |
10% TRITURADO |
DISCRETO |
1-2-3-4-5-8-10-12 |
SOLDADO |
|
LENTA |
|
|
|
|
|
|
BT |
POLIBUTENO 1 |
|
0.915 |
124-130 (FUS) |
|
|
290 |
270 |
260 |
240 |
40/80 |
|
|
1000/2000 |
50-70 % LARGA |
|
|
|
1.5-3.5 |
10% TRITURADO |
DISCRETO |
1-2-3-6 |
|
|
LENTA |
|
|
|
|
|
|
PIB |
POLI-ISO BUTILENO |
|
0.905-0.920 |
|
|
|
140-160 |
170-190 |
200-230 |
230-250 |
50-80 |
|
|
|
|
|
|
|
|
|
|
06-mar |
ES USADO COMO ADHESIVO |
|
LENTA |
|
|
|
|
|
|
PMP |
POLI
ISOBUTILENO-ETILENO |
|
0.83 |
235 (FUS) |
|
|
260-280 |
270-290 |
280-300 |
290-310 |
60/80 |
|
|
600-1200 |
50-70 % LARGA |
120/200 kg/cm² |
|
COLADA CAPILAR
C.C. |
1.5-3.5 |
10% TRITURADO |
DISCRETO |
02/01/2004 |
|
|
LENTA |
|
|
|
|
|
|
PTFE |
POLITETRAFLUOROETILENO |
|
2.1-2.3 |
NO FUNDE
CRISTALIZA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ÓPTIMO |
2 a 400°-450°-12 |
|
|
NO ARDE |
|
|
|
|
|
|
FEP |
COPOLÍMERO
TETRAFLUJO RETILENO-ESAFLUOROPR. |
|
2.13-2.16 |
285-295 (FUS) |
|
|
375 |
360 |
340 |
325 |
120/150 |
|
|
1000 |
|
|
ALTA |
|
3-4.5 |
|
ÓPTIMO |
02/01/2012 |
|
|
NO ARDE |
|
|
|
|
|
|
PCTFE |
POLICLOROTRIFLUORETILENO |
PCTFE |
2.11-2.13 |
270-310
REBLANDECE |
|
|
260 |
270 |
280 |
290 |
120/150 |
|
|
1500-3000 |
|
|
ALTA |
|
0.8-1.2 |
|
ÓPTIMO |
1-2-4 COMPRES. |
|
|
NO ARDE |
|
|
|
|
|
|
PVF |
POLIFLUORURO DE
VINIL |
|
1.38 |
171 REBLANDECE |
|
|
|
|
|
|
|
|
|
|
|
|
ALTA |
|
|
|
ÓPTIMO |
03-feb |
|
|
LENTA |
|
|
|
|
|
|
PVDF |
POLIFLUORURO DE
VINILIDENO |
|
1.75 |
171 (FUS) |
|
|
210-230 |
230-250 |
260-270 |
270-280 |
90/120 |
|
|
1000-1500 |
|
|
ALTA |
|
06-mar |
|
ÓPTIMO |
1 SÓLO CIL Y HUS. ESP. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
CA |
ACETATO DE
CELULOSA |
|
1.26-1.32 |
|
04-feb |
60-80 |
160-180 |
180-190 |
190-210 |
220-230 |
30/60 |
|
|
800-1500 |
|
|
|
|
0.3-0.6 |
|
DISCRETO |
1-2-3-4-5-12 COMP. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
CP |
PROPINATO DE
CELULOSA |
|
1.19-1.23 |
|
04-feb |
60-80 |
160-180 |
190-200 |
200-210 |
220-230 |
40/70 |
|
|
800-1500 |
|
|
|
|
0.3-0.6 |
|
DISCRETO |
1-2-3-8 |
|
|
LENTA |
|
|
|
|
|
|
CAB |
ACETATO BUTIRATO
DE CELULOSA |
|
1.16-1.21 |
|
04-feb |
60-80 |
160-180 |
180-190 |
190-210 |
220-230 |
40/70 |
|
|
800-1500 |
|
|
|
|
0.3-0.6 |
|
DISCRETO |
02/01/2008 |
|
|
LENTA |
|
|
|
|
|
|
EC |
ETICELULOSA |
|
1.09-1.17 |
|
3 |
60 |
230 |
210 |
190 |
175 |
60/80 |
|
|
800-1500 |
|
|
|
|
0.5-0.8 |
|
DISCRETO |
02/01/2003 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 66 |
POLIAMIDA (NYLON
66) |
PA 66 |
1.13-1.15 |
255-266 |
16-ago |
80-100 |
260-270 |
270-280 |
280-290 |
290-300 |
50/120 |
|
|
600-1200 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
0.8-2.5 |
20% |
DISCRETO |
1-3-4-5 TRITUR. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 DE
ALTO IMPACTO |
PA 66 HI |
1.08-1.10 |
240-260 |
16-ago |
80-100 |
270-280 |
280-290 |
290-300 |
300-310 |
50/120 |
|
|
70/1380 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
1.3-1.8 |
20% |
DISCRETO |
1-3-4-5 TRITUR. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
REFUERZO DE FIBRA DE VIDRIO |
PA 66 C FV |
1.38 |
265 |
16-ago |
80-100 |
270-280 |
280-285 |
285-295 |
290-300 |
50/120 |
|
|
350/1380 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
0.2-1.2 |
10% |
DISCRETO |
1-3-4-5 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 66/6 |
COPOLIAMIDA 66/6 |
PA 66/6 |
1.08-1.14 |
240 |
16-ago |
80-100 |
225-240 |
240-260 |
260-280 |
280-290 |
40/120 |
|
|
200/1050 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
0.6-1.5 |
10% |
DISCRETO |
1-3-4-5 TRITUR. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 6 |
POLIAMIDA (NYLON
6) |
PA 6 |
1.12-1.14 |
218-221 |
16-ago |
80-100 |
225-240 |
220-250 |
240-260 |
240-260 |
40/120 |
|
|
200-1200 |
BAJA |
30-130 |
ALTA |
CAPILAR SUBMARINO |
0.8-2.5 |
20% |
DISCRETO |
1-3-4-5 FILM |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 CON
REFUERZO DE FIBRA DE VIDRIO |
PA 6 C FV |
1.35-1.42 |
216 |
16-ago |
80-100 |
220-240 |
230-260 |
240-270 |
240-280 |
50/100 |
|
|
300-1200 |
BAJA |
30-130 |
ALTA |
CAPILAR SUBMARINO |
0.4-1.2 |
10% |
DISCRETO |
1-3-4-5 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 ALTO
IMPACTO |
PA 6 HI |
1.08-1.17 |
216 |
16-ago |
80-100 |
235-260 |
260-270 |
270-290 |
300-310 |
40/120 |
|
|
200-1200 |
BAJA |
30-130 |
ALTA |
CAPILAR SUBMARINO |
0.8-1.8 |
20% |
DISCRETO |
1-3-4-5 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 11 |
POLIAMIDA (NYLON
11) |
PA 11 INY |
1.03-1.05 |
185-188 |
06-abr |
70-80 |
190-200 |
210-220 |
220-240 |
250-260 |
40/80 |
|
|
600-1200 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
1-1.4 |
20% |
DISCRETO |
1-3-4-5-12 HILAD. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 6/10 |
POLIAMIDA (NYLON
610) |
PA 6/10 |
1.07-1.09 |
212-216 |
16-ago |
80-100 |
220-230 |
230-240 |
240-250 |
260-270 |
40/120 |
|
|
600-1200 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
0.8-2.0 |
20% |
DISCRETO |
1-3-4-5-12 HILAD. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 6/12 |
POLIAMIDA (NYLON
612) |
PA 6/12 |
1.06-1.08 |
208-212 |
16-ago |
80-100 |
220-230 |
230-240 |
240-250 |
260-270 |
40/120 |
|
|
600-1200 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
0.7-1.2 |
20% |
DISCRETO |
1-3-4-5-12 HILAD. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PA 12 |
POLIAMIDA (NYLON
12) |
PA 12 INY |
1.01-1.02 |
175-178 |
4 |
80-100 |
190-205 |
225-250 |
260-290 |
290-310 |
30/100 |
|
|
600-1200 |
BAJA |
50-150 |
ALTA |
CAPILAR SUBMARINO |
1.0-2.0 |
20% |
DISCRETO |
1-3-4-5-12 HILAD. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PU |
POLIURETANO |
PU |
1.25 |
|
|
|
200 |
190 |
185 |
175 |
20/45 |
|
|
800-1500 |
LAS PIEZAS
ESTAMPADAS SE TEMPLAN 15-20 h A 110°C |
|
ALTA |
|
02-ene |
TOTAL |
AMARILLEA |
1-2 COMP. HILAD. |
SIRVE COMO ADHESIVO |
|
LENTA |
|
|
|
|
|
|
PU |
POLIURETANO
LÍQUIDO |
LIQUID |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PU |
POLIURETANO
INSATURADO |
UNSATURATED |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PET |
POLIETILEN
TEREFTALATO |
PET |
1.34-1.38 |
250-260 |
12-feb |
12-feb |
270 |
270 |
265 |
260 |
140 |
|
|
800-1800 |
|
|
800-1800 |
|
2-2.2 |
TOTAL |
DISCRETO |
1-2-12 HILADO |
|
|
LENTA |
|
|
|
|
|
|
PET |
POLIETILEN
TEREFTALATO CON FIBRA DE VIDRIO |
PET FV |
1.34-1.38 |
250-260 |
12-feb |
12-feb |
270 |
270 |
265 |
260 |
140 |
|
|
800-1800 |
|
|
800-1800 |
|
0.2-2.2 |
|
DISCRETO |
1-2-12 HILADO |
|
|
LENTA |
|
|
|
|
|
|
PBT |
POLIBUTILENTEREFTALATO |
UNFILLED |
1.31 |
220-225 |
8 |
105 |
235 |
230 |
230 |
225 |
40/80 |
|
|
800-1400 |
|
|
ALTA |
|
1.7-2.3 |
TOTAL |
DISCRETO |
1-2-3-12 |
|
METALIZADO |
LENTA |
|
|
|
|
|
|
PBT |
POLIBUTILENTEREFTALATO
CON FIBRA DE VIDRIO |
PBT FV |
1.31 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0.5-1.5 |
|
|
|
|
|
|
|
|
|
|
|
|
PC |
POLICARBONATO
ALTA VISCOSIDAD |
PC HV |
1.2 |
220-230 |
08-abr |
100-120 |
270-280 |
290-300 |
300-310 |
320-330 |
80/110 |
|
|
800-2000 |
|
|
ALTA |
|
0.5-0.8 |
TOTAL |
CAMBIA COLOR |
1-2-3-12 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PC |
POLICARBONATO
BAJA VISCOSIDAD |
PC LV |
1.2 |
|
08-abr |
100-120 |
270-280 |
290-300 |
300-310 |
320-330 |
80/110 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PC/ABS |
ALEACIÓN
POLICARBONATO/ACRILONITRILO ESTIRENO BUTADIENO |
PC/ABS |
1.14 |
128 Vicat |
06-mar |
90-100 |
260-270 |
280-290 |
290-300 |
300-310 |
70/100 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC |
CLORURO DE
POLIVINIL |
PVC |
1.32-1.54 |
|
2 |
50 |
160-170 |
170-180 |
180-190 |
200-210 |
20/60 |
|
|
1000-1600 |
POCA |
MÁXIMO 50 kg/cm² |
MEDIA |
COLADA EN BLANCO |
0.5-0.8 |
100% SI NO ARDE |
AMARILLEA |
1-2-3-4-5-6-7-8-11-12 |
SOLDADO PEGADO |
METALIZADO |
NO ARDE |
|
|
|
|
|
|
PVC |
CLORURO DE
POLIVINIL (RÍGIDO) |
PVC R |
1.32-1.54 |
|
2 |
50 |
160-170 |
170-180 |
180-190 |
200-210 |
20/60 |
|
|
|
|
|
|
|
0.5-0.8 |
|
|
|
|
|
|
|
|
|
|
|
|
PVC |
CLORURO DE
POLIVINIL (FLEXIBLE, UNFILLED) |
PVC F |
1.16-1.35 |
|
|
|
140-160 |
160-170 |
170-180 |
190-200 |
20/60 |
|
|
|
|
|
|
|
0.7-3.0 |
|
|
|
|
|
|
|
|
|
|
|
|
PVC |
CLORURO DE
POLIVINIL (FLEXIBLE, FILLED) |
PVC F C CARGA |
1.16-1.35 |
|
|
|
140-160 |
160-170 |
170-180 |
190-200 |
20/60 |
|
|
|
|
|
|
|
0.5-1.5 |
|
|
|
|
|
|
|
|
|
|
|
|
PVCA |
CLORURO DE
POLIVINIL (COPOLÍMERO) |
|
1.32-1.54 |
|
2 |
50 |
190 |
170 |
160 |
140 |
20/40 |
|
|
ALTA |
|
|
|
|
05-ene |
100% SI NO ARDE |
AMARILLEA |
1-2-8 HILAD. CAL. |
SOLDADO PEGADO |
|
AUTOEXTIN. |
|
|
|
|
|
|
PVC-PP |
CLORURO VINILO
POLIPROPILENO (COPOLÍMERO) |
|
1.28-1.40 |
|
2 |
50 |
150-160 |
155-165 |
160-170 |
165-180 |
40/60 |
|
|
ALTA |
|
|
|
|
0.2-0.5 |
100% SI NO ARDE |
AMARILLEA |
04/03/2008 |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PV DC |
CLORURO DE
POLIVINILIDENO |
|
1.64-1.73 |
|
|
|
175 |
175 |
170 |
170 |
80/90 |
|
|
ALTA |
|
POCA |
BAJA |
|
0.2-0.5 |
|
AMARILLEA |
1-2-3-7 COMPR. |
|
|
AUTOEXTIN. |
|
|
|
|
|
|
PE OC |
POLIETERE
CLORURATO |
|
1.4 |
|
1 |
75 |
240 |
220 |
200 |
190 |
85/100 |
|
|
700-1400 |
|
MÁXIMO 50 kg/cm² |
BAJA |
COLADA LARGA |
0.4-0.8 |
100% SI NO ARDE |
ENDURECE |
1-2-4-8 COMPR. |
PEGADO SOLD. ULTRASONIDO |
|
AUTOEXTIN. |
|
|
|
|
|
|
PV CC |
CLORURO DE
POLIVINIL CLORURATO |
|
1.45-1.56 |
|
2 |
110 |
210 |
205 |
200 |
200 |
75/120 |
|
|
ALTA |
|
POCA |
BAJA |
COLADA LARGA |
0.3-0.7 |
100% SI NO ARDE |
AMARILLEA |
1-2-4-6-7 LAMIN |
PEGADO SOLD. ULTRASONIDO |
|
NO ARDE |
|
|
|
|
|
|
PPO |
POLIÓXIDO DE
FENILENO |
PPO |
1.06 |
110 |
04-feb |
100-110 |
250 |
270 |
290 |
300 |
80/110 |
|
|
1000-1400 |
|
|
ALTA |
|
0.5-0.9 |
|
BLANQUEA |
1-2-4-6-8-12 COMP. |
PEGADO SOLDADO |
METALIZADO |
AUTOEXTIN. |
|
|
|
|
|
|
PPO |
POLIÓXIDO DE
FENILENO (TRANSICIÓN VÍTREA BAJA) |
PPO LGT |
1.1 |
110 |
04-feb |
100-110 |
205 |
210 |
220 |
230 |
|
|
|
970/1400 |
|
|
ALTA |
|
0.5-0.7 |
|
BLANQUEA |
1-2-4-6-8-12 |
PEGADO SOLDADO |
METALIZADO |
AUTOEXTIN. |
|
|
|
|
|
|
PPO |
POLIÓXIDO DE
FENILENO (TRANSICIÓN VÍTREA ALTA) |
PPO HGT |
1.06 |
135 |
04-feb |
100-110 |
220 |
260 |
300 |
330 |
|
|
|
970/1400 |
|
|
ALTA |
|
0.5-0.8 |
|
BLANQUEA |
1-2-4-6-8-12 |
PEGADO SOLDADO |
METALIZADO |
AUTOEXTIN. |
|
|
|
|
|
|
PPO |
POLIÓXIDO DE
FENILENO (IMPACTO MODIFICADO) |
PPO IM |
1.27-1.36 |
135 |
04-feb |
100-110 |
220 |
240 |
260 |
290 |
|
|
|
690/1050 |
|
|
ALTA |
|
0.6 |
|
BLANQUEA |
1-2-4-6-8-12 |
PEGADO SOLDADO |
METALIZADO |
AUTOEXTIN. |
|
|
|
|
|
|
PPO |
POLIÓXIDO DE
FENILENO (30% FV) |
PPO FV |
1.08-1.09 |
100-110 |
04-feb |
100-110 |
260 |
280 |
300 |
330 |
|
|
|
1050/2800 |
|
|
ALTA |
|
0.1-0.4 |
|
BLANQUEA |
1-2-4-6-8-12 |
PEGADO SOLDADO |
|
AUTOEXTIN. |
|
|
|
|
|
|
PPS |
SULFURO DE
POLIFENILENO |
PPS |
1.34 |
288 |
06-mar |
140-250 |
310-330 |
340-350 |
360-370 |
370-380 |
25/130 |
|
|
800-1200 |
|
|
ALTA |
|
1 |
|
BLANQUEA |
1 COMPRESIÓN |
|
|
NO ARDE |
|
|
|
|
|
|
PSU |
POLISULFONO |
PSU |
1.25 |
190 |
04-mar |
120-150 |
330-340 |
350-360 |
360-380 |
380-390 |
90/150 |
|
|
1200-2000 |
|
|
ALTA |
|
0.6-0.8 |
|
AMALILLEA
ENDURECE |
1-2-4-8-12 |
|
METALIZADO |
AUTOEXTIN. |
|
|
|
|
|
|
PE |
POLIETILENO BAJA
DENSIDAD EXTRUSIÓN PELÍCULA |
LDPE EG |
0.92-0.93 |
105-115 |
|
|
40-60 |
120-140 |
140-170 |
150-180 |
160-190 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
20:1 A 28:1 |
2:1 A 3:1 |
|
1:1.7 A 1:2.3 |
40-70 |
|
LDPE |
POLIETILENO BAJA
DENSIDAD EXTRUSION PELICULA SACO USO RUDO |
LDPE F HD |
0.92-0.93 |
105-115 |
|
|
40-60 |
120-140 |
140-170 |
150-180 |
160-190 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
20:1 A 28:1 |
2:1 A 3:1 |
|
1:1.3 A 1:1.16 |
250 |
|
LDPE |
POLIETILENO BAJA
DENSIDAD INYECCIÓN |
LDPE IM |
0.92-0.93 |
105-115 |
|
|
120-170 |
150-200 |
170-210 |
180-220 |
20/80 |
|
|
600-1800 |
30-60 % |
150/230 kg/cm² |
NORMAL |
COLADA CAPILAR |
1.5-2 |
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
11:1 A 20:1 |
02:01 |
|
|
|
|
PE |
POLIETILENO BAJA
DENSIDAD EXTRUSIÓN LAMINACIÓN |
LDPE ELG |
0.92-0.93 |
105-115 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
P |
|
|
|
|
FPO |
ETILENO BUTIL
ACRILATO MODIFICADOR DE IMPACTO |
EBA |
0.93 |
66-78 |
3 |
70-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PEBA |
POLIETHER AMIDA
EN BLOQUE |
PEBA |
|
|
04-feb |
70-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPO |
ELASTÓMERO
TERMOPLÁSTICO POLIOLEFÍNICO |
TPO IM |
|
|
2 |
75 |
170-180 |
180-190 |
190-200 |
200-210 |
oct-80 |
|
|
|
|
|
|
|
1.5-2.0 |
|
|
|
|
|
|
|
|
|
|
|
|
TPE |
ELASTÓMERO
TERMOPLÁSTICO ESTIRÉNICO |
TPS |
|
|
|
|
170-180 |
180-190 |
200-210 |
210-230 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPU |
ELASTÓMERO
TERMOPLÁSTICO POLIURETÁNICO |
TPU |
1.2 |
|
.5-2 |
100-110 |
170-180 |
180-190 |
200-210 |
210-230 |
20-40 |
|
|
|
|
|
|
|
0.8-1.5 |
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD INYECCÓN COMPUESTO |
LDPE IM C |
0.92-0.93 |
105-115 |
|
|
120-170 |
150-200 |
170-210 |
170-220 |
20/80 |
|
|
600-1800 |
30-60 % |
150/230 kg/cm² |
NORMAL |
COLADA CAPILAR |
1.5-2 |
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
11:1 A 20:1 |
02:01 |
|
|
|
|
DULCE |
SDG |
DSFG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO EXTRUSIÓN |
ABS EG |
1.055 |
88-97 DTUL |
04-mar |
82-93 |
180-225 |
190-230 |
200-235 |
210-240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
18:1-24:1 |
2.8:1 |
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO PARA TUBERIA |
ABS EG P |
1.055 |
|
04-mar |
82-93 |
180-225 |
190-230 |
200-235 |
210-240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
18:1-24:1 |
2.8:1 |
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO CROMABLE |
ABS EP |
1.06 |
105-110 |
04-mar |
71-81 |
245-255 |
250-260 |
255-265 |
260-280 |
30-70 |
|
|
10000-16000 psi |
50-75% |
50-100 psi |
LENTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO ALTO BRILLO |
ABS HG |
1.055 |
101-105 |
04-mar |
74-81 |
INY 235-250 / EXT
71-93 |
INY 240-255 / EXT
74-96 |
INY 245-260 / EXT
77-99 |
INY 245-260 / EXT
82-105 |
INY 45-65 |
|
|
10000-16000 psi |
50-75% |
0-25 psi |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO ALTO IMPACTO, ALTO BRILLO |
ABS HI HG |
1.04 |
105 |
04-mar |
74-81 |
INY 235-250 / EXT
71-93 |
INY 240-255 / EXT
74-96 |
INY 245-260 / EXT
77-99 |
INY 245-260 / EXT
82-105 |
INY 45-65 |
|
|
10000-16000 psi |
50-75% |
0/50-25/100 psi |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO ALTO IMPACTO ALTA TEMPERATURA |
ABS HI HH |
1.05 |
116 |
04-mar |
75-90 |
230-245 |
235-250 |
245-255 |
245-260 |
40-70 |
|
|
13000-20000 psi /
50-70 kg/cm² |
50-75% |
25-100 psi / 5-15
kg/cm² |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO INYECCIÓN |
ABS IM |
1.05 |
106 |
4 |
71-77 |
235-255 |
240-255 |
245-260 |
245-265 |
45-65 |
|
|
10000-16000 psi |
50-75% |
50-100 psi |
ALTA |
|
|
|
|
|
|
|
|
|
02:01 |
60 rpm |
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO BAJO BRILLO |
ABS LG |
1.045 |
100-107 |
04-mar |
75-90 |
INY 235-250 / EXT
82 |
INY 240-255 / EXT
86 |
INY 245-260 / EXT
89 |
INY 245-260 / EXT
93 |
INY 45-65 |
|
|
10000-16000 psi |
50-75% |
50-100 psi |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO PARA REFRIGERACION |
ABS LT |
1.09 |
|
04-mar |
82-90 |
238 |
244 |
250 |
260 |
210-250 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO GRADO MEDICO |
ABS MED |
1.05 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO PINTABLE |
ABS PG |
1.06 |
110 |
4 |
71-77 |
245-255 |
250-260 |
255-265 |
255-265 |
50-60 |
|
|
10000-16000 psi |
50-75% |
50-100 psi |
LENTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO TRANSPARENTE |
ABS TR |
1.08 |
105 |
04-mar |
75-85 |
195-220 |
200-225 |
205-230 |
205-230 |
45-65 |
|
|
10000-16000 psi |
50-75% |
0-25 psi |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ABS |
ACRILONITRILO
ESTIRENO BUTADIENO-POLICARBONATO ALTA TEMPERATURA |
ABS/PC HH |
1.075 |
105 |
04-mar |
80-90 |
240-255 |
245-260 |
250-265 |
250-270 |
60-85 |
|
|
13000-20000 psi |
50-75% |
25-50 psi |
MODERADA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
ADA |
ACIDO ADIPICO |
ADA |
600-900 kg/cm³ |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ASA |
ACRILONITRILO
ESTIRENO ACRILATO ALTO IMPACTO |
ASA HI |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
CET |
ESTIRENO METIL
ACRILATO COPÓLIMERO ALTO IMPACTO |
CET IM |
1.05 |
88-91 |
02-ene |
60-80 |
|
|
|
|
32-82 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
EAMA |
ETILENO ESTER
ACRÍLICO CON ANHÍDRIDO MALÉICO |
EAMA IM |
0.94 |
65 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
EPS |
POLIESTIRENO
EXPANDIBLE |
EPS |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
EVOH |
ETILENO VINIL
ALCOHOL |
EVOH |
1.17-1.19 |
174-187 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
ADHESIVOS, TIE
LAYERS |
EAMA TL |
0.94 |
80-107 |
|
|
270-285 |
285-300 |
300-320 |
320-330 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
AGENTE DE
ACOPLAMIENTO Y COMPATIBILIZADORES |
EAMA AC |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
ETILENO ALPHA
OLEFINA (COP) PLASTOMERO DE POLIOLEFINA (POP) |
POP |
0.90-0.94 |
98 REBLANDECE
75-76 |
|
|
135 |
160 |
185 |
185 |
15-oct |
|
|
1000 |
|
|
LENTA |
CANAL CORIENTE |
0.7-0.9 |
|
DISCRETO |
1-2-3-4-8 |
|
|
LENTA |
|
|
|
|
|
|
FPO |
ETILENO METIL
ACRILATO COPOLÍMERO RANDOM |
EMA |
0.94 |
61-92 |
|
|
150 |
170 |
170 |
170 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
ETILENO METIL
ACRILATO-METACRILATO DE GLICIDILO |
EMA-GMA |
0.94 |
106 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
ETILENO VINIL
ACETATO MODIFICADO CON ANHÍDRIDO MALÉICO |
EVA-MAH |
0.95 |
75 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
IONOMERO |
EIM |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
POLIETILENO BAJA
DENSIDAD LINEAL MODIFICADO CON ANHÍDRIDO MALÉICO |
LLDPE-MAH |
0.913 |
118 |
|
|
160-180 |
180-200 |
200-220 |
210-230 |
220-240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
POLIETILENO
MODIFICADO CON ANHÍDRIDO MALÉICO |
PE-MAH |
0.885-0.910 |
75-119 |
|
|
210 |
220 |
230 |
230 |
240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GPPS |
POLIESTIRENO
CRISTAL INYECCIÓN |
GPPS IM |
1.04 |
82-98 Vicat |
04-feb |
71 |
171-199 |
193-227 |
218-254 |
204-232 |
38-82 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PE |
POLIETILENO ALTA
DENSIDAD COPOLÍMERO EXTRUSIÓN/SOPLO CUERPO HUECO |
HDP |
0.955 |
|
|
|
128 |
140 |
152 |
165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD COPOLÍMERO EXTRUSIÓN/SOPLO CUERPO HUECO FASE GAS |
HDPE CO BM G |
0.953 |
131 |
|
|
165 |
180 |
195 |
215 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD COPOLÍMERO INYECCIÓN |
HDPE CO IM |
0.953 |
131.2 |
|
|
232 |
243 |
246 |
246 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD COPOLIMERO INYECCION SOPLO |
HDPE CO IBM |
0.955 |
128-131 |
|
|
180 |
190 |
200 |
205 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD EXTRUSION |
HDPE EG |
0.949 |
128 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD EXTRUSIÓN PARA LÁMINA |
HDPE ESG |
0.918-0.953 |
84-127 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD EXTRUSION SOPLO HOMOPOLÍMERO PARA LECHE Y JUGO |
HDPE HO BM ALIM |
0.958 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD HOMOPOLÍMERO EXTRUSIÓN/SOPLO CUERPO HUECO |
HDPE HO BM |
0.96-0.964 |
129-132 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD HOMOPOLÍMERO INYECCIÓN |
HDPE HO IM |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD INYECCIÓN |
HDPE IM |
0.953-0.961 |
122-124 |
|
|
232 |
243 |
246 |
246 |
204-260 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
POLIETILENO ALTA
DENSIDAD PARA FILAMENTO |
HDPE FI |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR EXTRUSIÓN SOPLO C/H |
HMWPE BM |
0.948-0.951 |
122-126 Vicat |
|
|
204 |
219 |
234 |
249 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR PARA TUBERÍA BIMODAL |
HMWPE EG PI |
0.945-0.958 |
255 Vicat |
|
|
190 |
200 |
210 |
221 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR EXTRUSIÓN PELÍCULA |
HMWPE F |
0.937-0.951 |
129-131 |
|
|
180 |
200 |
220 |
230 |
|
|
|
|
|
|
|
|
|
|
|
03-feb |
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR PARA PELICULA BIMODAL |
HMWPE F BI |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO ALTA
DENSIDAD ALTO PESO MOLECULAR PARA PELICULA MONOMODAL |
HMWPE F MO |
0.952 |
125 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO MEDIO
PESO MOLECULAR, ALTA DENSIDAD PARA PELICULA |
MMWPE F |
0.947 |
127-130 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HMWPE |
POLIETILENO MEDIO
PESO MOLECULAR, MEDIA DENSIDAD PARA PELICULA |
MMW MDPE F |
0.937 |
126 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD COPOLIMERO EXTRUSIÓN SOPLO CON EVA |
LDPE CO C EVA |
0.923-0.926 |
88 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD EXTRUSIÓN |
LDPE EG |
0.918-0.927 |
111 |
|
|
170 |
120-140 |
140-170 |
150-180 |
170-190 |
|
|
|
|
|
|
|
|
100% TRITURADO |
DISCRETO |
1-2-3-4-5-7-8-10 |
PEGADO ARALDIT AW 10 |
BAJO VACÍO |
LENTA |
20:1 A 28:1 |
2:1 A 3:1 |
|
1:1.7 A 1:2.3 |
40-70 |
|
LDPE |
POLIETILENO BAJA
DENSIDAD INYECCIÓN |
LDPE IM |
0.919-0.925 |
111 |
|
|
163 |
177 |
177 |
177 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD INYECCÓN COMPUESTO |
LDPE IM C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD SIN ADITIVOS |
LDPE |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LLDPE |
POLIETILENO BAJA
DENSIDAD LINEAL ENTRECRUZABLE |
LLDPE X |
0.918 |
121 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LLDPE |
POLIETILENO BAJA
DENSIDAD LINEAL PARA INYECCIÓN |
LLDPE IM |
0.924-0.926 |
124 |
|
|
177 |
190 |
204 |
204 |
30-may |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LLDPE |
POLIETILENO BAJA
LINEAL DENSIDAD EXTRUSION LAMINACIÓN |
LLDPE ELG |
0.918 |
124 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LLDPE |
POLIETILENO BAJA
LINEAL DENSIDAD EXTRUSION PELICULA |
LLDPE F |
0.918-0.924 |
122 |
|
|
190 |
200 |
210 |
220 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
03-feb |
|
LLDPE |
POLIETILENO BAJA
LINEAL DENSIDAD EXTRUSION PELICULA USO RUDO |
LLDPE F HD |
0.918 |
122 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
30:01:00 |
|
|
|
6 IN |
|
LLDPE |
POLIETILENO
LINEAL BAJA DENSIDAD BUTENO |
LLDPE BUT |
0.9214 |
124 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MDPE |
POLIETILENO MEDIA
DENSIDAD INYECCIÓN |
MDPE IM |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MHDPE |
POLIETILENO ALTA
DENSIDAD METALOCENO |
MHDPE |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MIPS |
POLIESTIRENO
MEDIO IMPACTO |
MIPS |
1.03 |
83 Vicat |
|
|
210-227 |
216-232 |
216-232 |
27-204 |
38-82 |
|
|
10-21 MPa |
30-60% |
0-7 bar |
ALTA |
|
0.4-0.65 |
|
|
|
|
|
|
|
|
|
|
|
|
MLDPE |
POLIETILENO BAJA
DENSIDAD METALOCENO PARA PELICULA |
MLDPE F |
0.918-0.925 |
114 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MLLDPE |
POLIETILENO
METALOCENO LINEAL BAJA DENSIDAD EXTRUSIÓN PELÍCULA |
MLLDPE F |
0.915-0.933 |
108 |
|
|
170 |
185 |
200 |
220 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2.5:1 |
|
|
MMDPE |
POLIETILENO MEDIA
DENSIDAD METALOCENO |
MMDPE |
0.918-0.934 |
124 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MPP |
POLIPROPILENO
METALOCENO |
MPP |
0.9 |
152 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
COMPUESTO DE
POLIAMIDA 6 CON REFUERZO |
PA 6 C |
1.22 |
222 |
|
80 |
225-230 |
230-240 |
240-250 |
240-250 |
80-100 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 CON
CARGA DE TALCO |
PA 6 C CM T |
1.37 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 CON
CARGA MINERAL |
PA 6 C CM |
1.45 |
221 |
|
80 |
220-230 |
240-250 |
245-250 |
245-250 |
80-100 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 CON
REFUERZO DE FIBRA DE VIDRIO Y ESTABILIZADA AL CALOR |
PA 6 C FV HS |
1.38 |
222 |
|
80 |
225-230 |
230-240 |
240-250 |
240-250 |
80-100 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6 DE
ALTA VISCOCIDAD |
PA 6 HV |
1.14 |
222 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6 |
POLIAMIDA 6
ESTABILIZADA AL CALOR |
PA 6 HS |
1.46 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 6/3 |
COPOLIAMIDA 6/3 |
PA 6/3 |
1.12 |
155 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
FPO |
POLIPROPILENO
MODIFICADO CON ANHÍDRIDO MALÉICO |
PP-MAH |
0.905 |
127-167 |
|
|
210 |
220 |
230 |
230 |
240 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GPPS |
POLIESTIRENO
CRISTAL EXTRUSIÓN |
GPPS EG |
1.05 |
98-100 Vicat |
|
|
180 |
190 |
200 |
200 |
210 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GPPS |
POLIESTIRENO
CRISTAL PARA ALTA TEMPERATURA |
GPPS HH |
1.045 |
90-107 |
|
|
Ext 180 |
Ext 190 |
Ext 200 |
Ext 200 |
Ext 210 / Iny
38-82 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GPPS |
POLIESTIRENO
CRISTAL PARA ESPUMADO |
GPPS E |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
GPPS |
POLIESTIRENO
CRISTAL PARA LAMINA O PELICULA OPS |
GPPS EG OPS |
1.05 |
98-100 Vicat |
|
|
180 |
190 |
200 |
200 |
210 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HDPE |
COMPUESTO DE
POLIETILENO ALTA DENSIDAD PARA TUBERÍA |
HDPE EG T |
0.944-0.959 |
190-220 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HIPS |
POLIESTIRENO ALTO
IMPACTO EXTRUSIÓN |
HIPS EG |
1.05 |
90-100 |
|
|
177-193 |
182-204 |
188-210 |
199-216 |
19-232 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HIPS |
POLIESTIRENO
SUPER ALTO IMPACTO EXTRUSIÓN |
HIPS HI EG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HIPS |
POLIESTIRENO ALTO
IMPACTO INYECCIÓN |
HIPS IM |
1.045 |
80-100 Vicat |
|
|
218-249 |
218-249 |
199-213 |
213-243 |
38-82 |
|
|
|
|
25-175 psi |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
HIPS |
POLIESTIRENO
SUPER ALTO IMPACTO INYECCIÓN |
HIPS SHI IM |
1.04 |
95 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD EXTRUSIÓN LAMINACIÓN |
LDPE ELG |
0.917-0.920 |
105-108 |
|
|
240 |
290 |
320 |
320 |
310 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
30:01:00 |
|
|
2,5:1 |
6 IN |
|
PA 66 |
COMPUESTO DE
POLIAMIDA 66 CON REFUERZO |
PA 66 C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
CARGA MINERAL |
PA 66 C CM |
1.14 |
263 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
CARGA MINERAL Y REFUERZO DE FIBRA DE VIDRIO |
PA 66 C FV CM |
1.24 |
263 |
|
80 |
260-270 |
270-280 |
280-290 |
280-290 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
RETARDANTE A LA FLAMA Y REFUERZO DE FIBRA DE VIDRIO |
PA 66 C FV FR |
1.17 |
263 |
|
80 |
270-275 |
275-280 |
280-285 |
280-285 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 DE
ALTO IMPACTO CON REFUERZO DE FIBRA DE VIDRIO |
PA 66 C FV HI |
1.12 |
260 |
|
|
230-260 |
250-270 |
260-280 |
260-270 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
REFUERZO DE FIBRA DE VIDRIO Y ESTABILIZADA AL CALOR |
PA 66 C FV HS |
1.24 |
263 |
06-feb |
80 |
260-270 |
270-280 |
280-290 |
280-290 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
ESTABILIZADOR AL CALOR |
PA 66 HS |
1.14 |
263 |
|
80 |
250-270 |
260-280 |
270-290 |
270-290 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
ALTA VISCOSIDAD |
PA 66 HV |
1.14 |
263 |
|
80 |
260-270 |
270-280 |
280-290 |
280-290 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
BAJA VISCOSIDAD |
PA 66 LV |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA 66 |
POLIAMIDA 66 CON
RETARDANTE A LA FLAMA |
PA 66 RF |
1.17 |
263 |
|
80 |
270-275 |
275-280 |
280-285 |
280-285 |
60-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA11 |
POLIAMIDA 11 EN
POLVO |
PA 11 POWDER |
0.43 |
183-188 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA11 |
POLIAMIDA 11 PARA
EXTRUSIÓN |
PA 11 EG |
1.04 |
181 |
08-abr |
80-90 |
230 |
250 |
280 |
280 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA12 |
POLIAMIDA 12 |
PA 12 |
1.05 |
181 |
06-abr |
80-90 |
270 |
280 |
290 |
290 |
40-80 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PA12 |
POLIAMIDA 12 EN
POLVO |
PA 12 G |
1.04 |
177-181 |
08-abr |
80-90 |
230 |
250 |
280 |
280 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PAN |
POLIACRILONITRILO |
PAN |
1.15 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PBT COMP |
COMPUESTO DE
POLIBUTILEN TEREFTALATO CON FIBRA DE VIDRIO |
PBT C |
1.53 |
223 |
08-abr |
120 |
230-240 |
235-250 |
235-250 |
240-260 |
60-100 |
|
|
35-125 BAR |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PBT-PC |
POLIBUTILEN
TEREFTALATO-POLICARBONATO ALEACION |
PBT-PC |
1.3 |
135 Vicat |
04-mar |
120 |
240-255 |
245-260 |
250-265 |
245-260 |
65-90 |
|
|
|
|
0.3-0.7 MPa |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA CO |
POLIMETIL
METACRILATO MEDIO IMPACTO Y RESISTENCIA TÉRMICA |
PMMA HH MI |
1.17 |
99-110 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
GRANULADO DE
LAMINA |
PMMA GR |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETEL
METACRILATO PARA EXTRUSIÓN PARA CUBIERTA |
PMMA EG S |
1.15 |
70-91 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO ALTA RESISTENCIA QUÍMICA Y TÉRMICA |
PMMA CR HH |
1.19 |
111 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO ALTO FLUJO Y RESISTENCIA QUIMICA |
PMMA HF CR |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO ALTO IMPACTO ALTA RESISTENCIA TERMICA |
PMMA HI CR |
1.19 |
11 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO CON ALTA RESISTENCIA QUIMICA |
PMMA CR |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO CON ALTO FLUJO |
PMMA HF |
1.18 |
88 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO COPOLÍMERO INYECCIÓN ALTO IMPACTO Y RESITENCIA QUIMICA |
PMMA CO HI CR |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO PARA EXTRUSIÓN |
PMMA EG |
1.15 |
98 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA HO |
POLIMETIL
METACRILATO PARA INYECCIÓN |
PMMA |
1.19 |
103 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
POM |
COMPUESTO DE
POLIÓXIDO DE METILENO |
POM COMP |
1.41 |
166 |
3 |
80-100 |
170-180 |
180-190 |
180-190 |
190-200 |
|
|
|
600-1200 BAR |
|
0-5 BAR |
LENTA-MEDIA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP COMP |
POLIPROPILENO
CARGADO CON CACO3 |
PP C CACO3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP COMP |
POLIPROPILENO
CARGADO CON TALCO |
PP C CM T |
0.97-1.16 |
140 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP COMP |
POLIPROPILENO
CARGADO CON FIBRA DE VIDRIO |
PP C FV |
0.9 |
148 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP COMP |
COMPUESTO DE
POLIPROPILENO OTROS |
PP COMP |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP COMP |
COMPUESTO DE
POLIPROPILENO AUTOMOTRIZ |
PP COMP IM A |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO EXTRUSIÓN SOPLO C/HUECO |
PP HO BM |
0.902-0.905 |
165 |
|
|
145-200 |
210-235 |
210-235 |
210-235 |
23-50 |
|
|
|
30-60% |
50-150 psi |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO CLARIFICADO |
PP HO CL |
0.905 |
153 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO EXTRUSIÓN |
PP HO EG |
0.91 |
165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO EXRUSIÓN PARA BOPP |
PP HO EG BOPP |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO FILAMENTO/RAFIA |
PP HO EG S |
0.905 |
165 |
|
|
210 |
220 |
235 |
250 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PPS |
SULFURO DE
POLIFENILENO COMPUESTO CON CARGA MINERAL |
PPS C CM |
1.95 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PPS |
SULFURO DE
POLIFENILENO COMPUESTO CON FIBRA DE VIDRIO |
PPS C FV |
1.65 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO
FLEXIBLE DE CLORURO DE POLIVINIL EXTRUSIÓN |
PVC C FEG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO
FLEXIBLE DE CLORURO DE POLIVINIL INYECCIÓN |
PVC C F IM |
1.18-1.25 |
|
|
|
145 |
155 |
165 |
180 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO
FLEXIBLE DE CLORURO DE POLIVINIL PARA ROTOMOLDEO |
PVC C F RO |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO RIGIDO
DE CLORURO DE POLIVINIL EXTRUSIÓN |
PVC C R EG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO RIGIDO
DE CLORURO DE POLIVINIL EXTRUSIÓN ETIQUETAS |
PVC C R EL |
1.30-1.33 |
|
|
|
150 |
165 |
180 |
190 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO RIGIDO
DE CLORURO DE POLIVINIL EXTRUSIÓN SOPLO |
PVC C R BM |
1.32 |
|
|
|
150 |
165 |
180 |
190 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC C |
COMPUESTO RIGIDO
DE CLORURO DE POLIVINIL INYECCIÓN |
PVC C R IM |
1.40-1.44 |
|
|
|
145 |
155 |
165 |
175 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC P |
CLORURO DE
POLIVINIL EN POLVO |
PVC P |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PVC R |
CLORURO DE
POLIVINIL RESINA |
PVC RES |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SBC |
ESTIRENO
BUTADIENO COPOLÍMERO ADITIVO CONCENTRADO |
SBC A |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SBC |
ESTIRENO
BUTADIENO COPOLÍMERO EN BLOQUE RIGIDO |
SBC R |
1.01 |
89-93 Vicat |
|
|
INY 180 / EXT 190 |
INY 200 / EXT 200 |
INY 225 / EXT 215 |
INY 250 / EXT 230 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SBC |
ESTIRENO
BUTADIENO COPOLÍMERO EN BLOQUE SEMIFLEXIBLE |
SBC SF |
1.01 |
80.6-87 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SEBS |
ESTIRENO ETILENO
BUTILENO ESTIRENO |
SEBS |
0.99-1.16 |
|
|
|
INY 155-175 / EXT
150-170 |
INY 165-185 / EXT
155-175 |
INY 175-195 / EXT
165-185 |
INY 195-225 /
EXT175-205 |
INY 25-50 / EXT
190-210 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LDPE |
POLIETILENO BAJA
DENSIDAD EXTRUSION PELICULA SACO USO RUDO |
LDPE F HD |
0.921 |
111 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
30:01:00 |
|
|
2,5:1 |
6 IN |
|
PC |
POLICARBONATO
PARA ALTA TEMPERATURA |
PC HT |
1.19 |
140 Vicat |
04-mar |
100-120 |
250-270 |
260-280 |
270-295 |
265-290 |
70-95 |
|
|
|
|
0.3-0.7 MPa |
40-70 rpm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PET-A |
POLIETILEN
TEREFTALATO AMORFO |
PET-A |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PET-C |
COMPUESTO
POLIETILEN TEREFTALATO CON FIBRA DE VIDRIO |
PET C FV |
1.56 |
|
4 |
120 |
|
|
|
|
>95 |
|
|
35-140 MPa |
|
|
RAPIDA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PMMA CO |
POLIMETIL
METACRILATO ALTA RESISTENCIA FROSTED |
PMMA HI FRO |
1.15 |
98 Vicat |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO PARA LAMINACIÓN TERMOFORMADO |
PP HO ELG T |
0.905 |
165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO PARA TELA NO TEJIDA |
PP HO H |
0.905 |
165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO INYECCIÓN |
PP HO IM |
0.905 |
152 Vicat |
|
|
200 |
210 |
220 |
225 |
15-40 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP HO |
POLIPROPILENO
HOMOPOLÍMERO NUCLEADO |
PP HO N |
0.905 |
158-165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO EXTRUSIÓN SOPLO |
PP IMCO BM |
0.905 |
160-165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO EXTRUSIÓN LAMINA CORRUGADA |
PP IMCO ELG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO EXTRUSIÓN LAMINA Y TERMOFORMADO |
PP IMCO ELG T |
0.905 |
160-165 |
|
|
|
|
|
|
20-50 |
|
|
12100 psi |
|
|
|
|
|
|
|
|
|
|
|
16.0:1 to 24.0:1.0 |
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO INYECCIÓN |
PP IMCO IM |
0.987-0.905 |
148 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO INYECCIÓN PARA PARED DELGADA |
PP IMCO IM PD |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP IMCO |
POLIPROPILENO
COPOLÍMERO IMPACTO NUCLEADO |
PP IMCO N |
0.905 |
160-165 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM EXTRUSIÓN/SOPLO CUERPO HUECO |
PP RACO BM |
0.9 |
143 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM CLARIFICADO |
PP RACO CL |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM EXTRUSIÓN TERMOFORMADO |
PP RACO EG T |
0.9 |
147 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM INYECCIÓN |
PP RACO IM |
0.9 |
149 |
|
|
200 |
210 |
215 |
225 |
15-40 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PP RACO |
POLIPROPILENO
COPOLÍMERO RANDOM NUCLEADO INYECCIÓN |
PP RACO IM N |
0.9 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SAN |
ESTIRENO
ACRILONITRILO ALTA CLARIDAD |
SAN HC |
|
140 Vicat |
04-mar |
75-80 |
170 |
185 |
200 |
210 |
40-60 |
|
|
50-70 kg/cm² |
40-60 kg/cm² |
5-15 kg/cm² |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SAN |
ESTIRENO
ACRILONITRILO ALTA RESISTENCIA A QUIMICOS |
SAN CR |
1.07 |
107 Vicat |
2 |
180-190 |
175-185 |
190-200 |
205-215 |
205-215 |
50-80 |
|
|
10000-20000 psi |
40-80% |
0-25 psi |
ALTA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
TPE |
ELASTÓMERO
TERMOPLÁSTICO ESTIRÉNICO |
TPS SBS |
1.02-1.15 |
|
1 |
60 |
130-140 |
140-150 |
150-160 |
160-165 |
45 |
|
|
30-40 psi |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPV |
ELASTÓMERO
TERMOPLÁSTICO DE HULE VULCANIZADO |
TPV |
0.96 |
|
03-feb |
90 |
INY 155-175 / EXT
160-180 |
INY 165-185 / EXT
165-185 |
INY 170-190 / EXT
170-190 |
INY 180-210 / EXT
185-205 |
INY 25-50 / EXT
195-225 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
UHMWPE |
POLIETILENO ULTRA
ALTO PESO MOLECULAR |
UHMWPE |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ULDPE |
POLIETILENO ULTRA
BAJA DENSIDAD |
ULDPE |
0.905 |
123 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
LLDPE |
POLIETILENO
LINEAL BAJA DENSIDAD HEXENO |
LLDPE HEX |
0.918-0.935 |
124 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
30:01:00 |
|
|
|
6 IN |
|
LLDPE |
POLIETILENO
LINEAL BAJA DENSIDAD OCTENO |
LLDPE OCT |
0.917-0.920 |
123 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
30:01:00 |
|
|
|
|
|
MBS |
METACRILATO
BUTADIENO ESTIRENO |
MBS (SBMMA) |
1.05 |
99 Vicat |
2 |
65 |
179-213 |
185-218 |
191-224 |
191-224 |
27-54 |
|
|
|
|
100 psi |
MODERADA A ALTA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MDLPE |
POLIETILENO MEDIA
DENSIDAD LINEAL PARA ROTOMOLDEO |
MDLPE RO |
0.9365 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MDPE |
POLIETILENO MEDIA
DENSIDAD EXTRUSIÓN PELÍCULA |
MDPE EG F |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MDPE |
POLIETILENO MEDIA
DENSIDAD EXTRUSIÓN/SOPLO CUERPO HUECO |
MDPE BM |
0.92-0.95 |
125 Vicat |
|
|
180 |
190 |
200 |
210 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MMWPE |
POLIETILENO ALTA
DENSIDAD MEDIO PESO MOLECULAR PARA PELÍCULA |
HDPE MMW F |
0.958-0.961 |
130-134 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
MMWPE |
POLIETILENO MEDIA
DENSIDAD MEDIO PESO MOLECULAR |
MDPE MMW |
0.937 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PC |
POLICARBONATO
EXTRUSIÓN |
PC EG |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
PC |
POLICARBONATO
INYECCIÓN |
PC IM |
1.2 |
147-153 Vicat |
05-mar |
100-120 |
235-260 |
250-275 |
265-290 |
265-300 |
65-105 |
|
|
|
|
0.25-0.7 MPa |
40-70 rpm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPO |
ELASTÓMERO
TERMOPLÁSTICO POLIOLEFÍNICO |
TPO |
0.88-1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPO |
ELASTÓMERO
TERMOPLÁSTICO POLIOLEFÍNICO PARA SELLADO |
TPO S |
0.902 |
133 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPO |
ELASTÓMERO
TERMOPLÁSTICO POLIOLEFÍNICO TACTO SUAVE |
TPO TS |
0.88 |
140 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SIS |
ESTIRENO
ISOPROPENO ESTIRENO |
SIS |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
SMA |
ESTIRENO
ANHÍDRIDO MALÉICO |
SMA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
S-MAH |
ESTIRENO-ANHÍDRIDO
MALÉICO |
S-MAH |
|
|
03-feb |
82-93 |
240-255 |
245-260 |
250-265 |
250-265 |
60-85 |
|
|
|
|
25-50 psi |
MODERADA |
|
|
|
|
|
|
|
|
20:01 |
|
|
|
|
|
SMMA |
ESTIRENO METIL
METACRILATO |
SMMA |
1.07-1.09 |
104-16 Vicat |
2 |
82 |
182-216 |
199-232 |
210-243 |
210-243 |
|
|
|
|
|
MODERADA |
LENTA A MODERADA |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPA |
POLIETER AMIDA EN
BLOQUE |
PEBA |
1.01 |
134-172 |
07-may |
70-80 |
INY 230 / EXT 220 |
INY 260 / EXT 235 |
INY 290 / EXT 250 |
INY 290 / EXT 250 |
25-60 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TPC |
ELASTÓMERO
TERMOPLÁSTICO DE COPOLIESTER |
TPC |
1.17 |
150 |
03-feb |
80 |
|
|
|
|
30-40 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|